ZrW2O8

A recent study [1] of ZrW2O8, investigated the amorphous phase that can be recovered after its high-pressure amorphization transition above 1.5 GPa. Reverse Monte Carlo modelling of neutron and ID31 data shows that the large increase in density on pressurising is accommodated within the structure by increased bonding between the WO4 tetrahedra. This increases the tungsten coordination; postulated changes to the ZrO6 octahedral environment are not required. This densified crystal based model, which contains significant local disorder within a distorted periodic structure, was also in keeping with data measured in situ at high pressure.

ZrW2O8_figure-resize367x200.png

Figure 1: Polyhedral representation of a section of (a) α-ZrW2O8 and (b) amorphous ZrW2O8 from RMC refinement of model B [1].

[1]  Structural Description of Pressure-Induced Amorphization in ZrW2O8.  D. A. Keen, A. L. Goodwin, M. G. Tucker, M. T. Dove, J. S. O. Evans, W. A. Crichton, and M. Brunelli, Phys. Rev. Lett., 98, 225501 (2007).

(top)
 

Semiconducting selenium nanoparticles

Combining Rietveld analysis with PDF analysis can be advantageous for crystalline materials with short-range order representing deviations from the average (crystallographic) structure. Thus the structural properties of semiconducting nanoparticles of selenium grown in the pores of a neodymium zeolite-Y were investigated using this approach [2]. Powder diffraction patterns were measured at 41 keV (0.298 Å) up to 110° in 2θ and the average structure refined, which included three Se sites forming a cluster in the large (13 Å diameter) cavity of the zeolite. The clusters however contain vacancies, and relaxation in the Se positions is then expected. Indeeed the Se atoms had large temperature factors in an attempt to model this disorder. 

Se_nanoparticles_fig2.-crop491x364-resize269x200.PNGSe_nanoparticles_fig1-resize395x200.jpeg

Figure 2. (left) Rietveld fit and (right) average structure of Se nanoparticles in Nd-zeolite-Y, [6].

According to the chemical composition, 32% of the cages can be filled. PDF analysis, which includes the evident diffuse scattering from short-range order, indicated that the average structure was adequate on the length scale from 8 - 50 Å, suggesting that correlations between clusters in adjacent cages via the framework are not important. On the 1 - 8 Å scale however, deviations from the average structure are evident. The PDF was used to extract a model of the short-range order within the Se clusters, and to account for correlations between the Se clusters and the framework, which can relax under the influence of the clusters.

[2] From average to local structure: A Rietveld and an atomic pair distribution function (PDF) study of selenium clusters in zeolite-NdY. Abeykoon A.M.M., Donner W., Brunelli M., Castro-Colin M., Jacobson A.J., Moss S.C. J. Am. Chem. Soc. 131, 13230, (2009).
 

(top)

 


References:

[1]  Structural Description of Pressure-Induced Amorphization in ZrW2O8.  D. A. Keen, A. L. Goodwin, M. G. Tucker, M. T. Dove, J. S. O. Evans, W. A. Crichton, and M. Brunelli, Phys. Rev. Lett., 98, 225501 (2007).

[2] From average to local structure: A Rietveld and an atomic pair distribution function (PDF) study of selenium clusters in zeolite-NdY. Abeykoon A.M.M., Donner W., Brunelli M., Castro-Colin M., Jacobson A.J., Moss S.C. J. Am. Chem. Soc. 131, 13230, (2009).